| Copper Chromium Zirconium (C18150/CuCrZr/CW106C/2.1293) |
| Chemical composition(%) |
| Cr | 0.5 - 1.5 |
| Zr | 0.02 - 0.2 |
| Cu | Balance |
| Material characteristics |
| Corrosion resistant |
| High electrical conductivity |
| High strength |
| High hardness |
| Deformation resistant |
| Resistance welding electrodes |
| Seam welding |
| Flash and butt welding dies |
| Welding gun arms, welding platens, molds, spot welding tips, seam welding shafts |
| Caps and shanks, Circuit breaker parts |
| Collector connector, collector housing, connector bar, connector lead bars |
| Cross-wire welding electrodes and components, Electrode holders and adaptors, Power generation products, |
| Transmission devices |
| Form | Temper | Temper code | Tensile strength (KSI) | YS-0.5% Ext(KSI) | Elongation(%) | Rockwell B scale | Section size(in) |
| Rod | Precipitation heat treated or spinodal heat treated and hard | TL04 | 81 Typ | 79 Typ | 14 Typ | 82 Typ | 0.485 |
| Precipitation heat treated or spinodal heat treated and hard | TL04 | 79 Typ | 75 Typ | 16 Typ | 78 Typ | 0.75 | |
| Spinodal hardened-low strength(ATLS) | TX00 | 65 Min | 55 Min | 13 Typ | 75 Typ | 1.0 | |
| Wire | Precipitation heat treated or spinodal heat treated and 1/2 hard | TL02 | 68 Typ | 58 Typ | 19 Typ | 75 Typ | 0.6 |
| Precipitation heat treated or spinodal heat treated and 1/2 hard | TL02 | 69 Typ | 49 Typ | 15 Typ | 76 Typ | 0.7 | |
| Precipitation heat treated or spinodal heat treated and hard | TL04 | 68 Typ | 66 Typ | 15 Typ | 73 Typ | 0.5 | |
| Precipitation heat treated or spinodal heat treated and hard | TL04 | 68 Typ | 63 Typ | 20 Typ | 74 Typ | 0.6 |
| * Measured at room temperature , 68F(20C) |
| Chromium Zirconium Copper general introduction |
|
Chromium zirconium Alloy C18150 has good thermal and electrical conductivity. More than 400 types of these copper alloys are available, but C18150 is highly preferred since it has high strength and wear resistance at elevated temperatures. C18150 is used extensively for cap-style resistance welding electrodes. In some specific situations, it can provide less sticking and resist deformation for much longer than its copper-chrome counterpart. The chemical composition of C18150 is 1% chromium, 98.85% copper, and 0.15% zirconium. The addition of Zirconium to chromium copper improves creep resistance at high operating temperatures and reduces the sticking of electrodes to the work during spot welding of galvanized or coated materials. The physical copper properties of C18150 include a density of 8.89 grams per cubic centimeter. TYPICAL USES OF CHROMIUM ZIRCONIUMSTRESS RELAXATIONChromium zirconium is a unique copper alloy that's able to decrease stress under constant strain. It's typically used with steel bolts in turbine casting, which must be straightened and typed. MACHININGMachining includes a variety of processes in which a raw piece of material is cut into a desired final shape and size by a controlled material-removal process. The machinability rating of C18150 is 30% which is moderate. The use of a cutting tool with a chip breaker is recommended. MATERIAL PROPERTIES OF C18150The C18150 copper alloy has a combination of properties as below:
FABRICATION PROPERTIESThe most common fabrication properties of C18150 are bending cold heading, and machining. The machinability rating of C18150 is 20. The fabrication properties of C18150 Copper can be categorized as either good, not recommended, fair, or excellent. The properties are as follows:
|